ASTM TYPE I/II

PRODUCTS

ASTM-C-150

STANDARD

28/02/2020

UPDATE

Portland cement; limestone, marl, clay, iron ore, pyrite ash, bauxite, etc. at appropria te proportions of raw materials, milling, cooking of the clinker obtained, the amount of retarder (generally composed of a ground with gypsum); It is the product gains strength after a certain time being mixed with water. In general, the structures that require high strength, cold weather in poured concrete, prefabricated structures, tunnels – in the mold applications, construction chemicals used in the manufacture and application of concrete foundation.

Physical Properties

Nuh Çimento San. A.Ş. Standard Unit
Initial Setting Time 100-150 min.45 minute
Final Setting Time 160-240 - minute
Specific Gravity 3,15-3,25 - g/cm3
Soundness 0-2 max.10 mm
Air Content 3-5 max.12 %
Autoclave 0,15-0,30 max.0,80 %
Specific Surface Area (Blaine) 3600-4100 min.2800 cm2/g
Bulk Density 950-1050 - g/l
3 Days Strength 24,0-31,0 min.10,0 MPa
7 Days Strength 31,0-38,0 min.17,0 MPa
28 Days Strength 38,0-48,0 - MPa

Chemical Properties

Nuh Çimento San. A.Ş. Standard Unit
Al2O3 4,00-5,00 max.6,00 %
Fe2O3 3,50-4,00 max.6,00 %
MgO 1,20-2,00 - %
SO3 2,30-2,80 max.3,00 %
Loss on Ignition 1,50-2,90 max.3,00 %
Insoluble Residue 0,20-0,50 max.0,75 %
Cl- 0,0050-0,0200 max.0,10 %
Alkali Equivalent Na2O + 0.658 K2O 0,45-0,55 max. 0,60 %
C3S 60-70 - %
C3A 5,00-6,00 max.8,00 %

It can be put on the market as bulk, in 1,5 ton big bags, in sling bags and also in 25 and 50 kg bags.

PACKAGING

Our product is certified by British Standard Institute (B.S.I.) according to ASTM C150 to use ASTM marking.

QUALITY CONTROL

Abdulhamit AKÇAY, Sales Director ( Export ), Internal Telephone 2075

FOR INFORMATION

It is updated on 28/02/2020.

UPDATE

The product specifications described above are intended solely for the purpose of informing customers and our company does not assume any responsibility.

ASTM TYPE IL

PRODUCTS

ASTM-C-595

STANDARD

01/05/2023

UPDATE

It is the product that is obtained by grinding Portland cement clinker together with a certain amount of set regulator (gypsum) with additives (limestone) at the rate defined in the standards (min 5% -max 20%) and gains strength by freezing after a certain period of time by mixing with water.

Physical Properties

Physical Properties Standard Unit
Setting Time Initial Min. 45 Minute
Setting Time Final Minute
Specific Gravity g/cm³
Air Content Max. 12 %
Autoclave Expansion Max. 0,80 mm
Specific Surface cm²/g
3 Days Strength Min. 13 Mpa
7 Days Strength Min. 20 MPa
28 Days Strength Min. 25 MPa

Chemical Properties

Chemical Properties Standard Unit
SO₃ Max. 3.0 %
Loss on Ignition Max. 10.0 %
Limestone Content Min. 5-15 %

It can be put on the market as bulk, in 1,5 ton big bags, in sling bags and also in 25 and 50 kg bags.

PACKAGING

Our product is certified by British Standard Institute (B.S.I.) according to ASTM C595

QUALITY CONTROL

Abdulhamit AKÇAY, Sales Director ( Export ), Internal Telephone 2075

FOR INFORMATION

It is updated on 01/05/2023.

UPDATE

The product specifications described above are intended solely for the purpose of informing customers and our company does not assume any responsibility.

CEM I 42,5 R

PRODUCTS

EN 197-1:2011

STANDARD

28/02/2020

UPDATE

Portland cement; limestone, marl, clay, iron ore, pyrite ash, bauxite, etc. at appropria te proportions of raw materials, milling, cooking of the clinker obtained, the amount of retarder (generally composed of a ground with gypsum); It is the product gains strength after a certain time being mixed with water. In general, the structures that require high strength, cold weather in poured concrete, prefabricated structures, tunnels – in the mold applications, construction chemicals used in the manufacture and application of concrete foundation.

Physical Properties

Nuh Çimento San. A.Ş. Standard Unit
Initial Setting Time 135 - 180 min.60 minute
Final Setting Time 190 - 230 - minute
Specific Gravity 3,16 - 3,21 - g/cm3
Soundness 0 - 2 max.10 mm
Specific Surface Area (Blaine) 3500 - 4000 - cm2/g
Bulk Density 980 - 1030 - g/l
2 Days Strength 26,0 - 35,0 min.20 MPa
28 Days Strength 56,0 - 61,0 42,5-62,5 MPa

Chemical Properties

Nuh Çimento San. A.Ş. Standard Unit
SO3 2,40 - 3,20 max.4,00 %
MgO 1,40 - 2,00 - %
Loss on Ignition 2,00 - 2,80 max.5,00 %
Insoluble Residue 0,20 - 0,80 max.5,00 %
Cl- <0,05 max.0,10 %
Alkali equivalent Na2O + 0.658 K2O 0,40 - 0,80 - %
Free Lime 1,00 - 1,80 - %

* Can be available with Low Hexavalent Chromium content (below 2 ppm) and Low Alkali Equivalent content (below 0,60 %).

It can be put on the market as bulk, in 1,5 ton big bags, in sling bags and also in 25 and 50 kg bags.

PACKAGING

Our product has EC certificate given by the Council for Quality and Environment (CQE) and has the right to use CE mark.

QUALITY CONTROL

Abdulhamit AKÇAY, Sales Director ( Export ), Internal Telephone 2075

FOR INFORMATION

It is updated on 28/02/2020.

UPDATE

The product specifications described above are intended solely for the purpose of informing customers and our company does not assume any responsibility.

CEM 1 52.5 N

PRODUCTS

EN 197-1:2011

STANDARD

28/02/2020

UPDATE

Portland cement is the product, produced by grinding clinker manufactured by burning raw materials like limestone, marl, clay, iron ore, pyrite ash, bauxite at appropriate proportions and by addition of a certain amount of retarder (generally gypsum) and sets and gains strength after a certain time being mixed with water.

It is generally used in works requiring higher strentgh values, concrete works at low temperatures, precast buildings, tunnel-form applications, building chemical manufacturing and foundations.

Additionnaly, it is suitable to be used in sea water . Mineralogical composition of this cement permits to be resistant to sulfate ions in presence of chloride ions.

Physical Properties

Nuh Çimento San. A.Ş. Standard Unit
Initial Setting Time 120 - 180 min.45 minute
Final Setting Time 150 - 250 - minute
Specific Gravity 3,16 - 3,21 - g/cm3
Soundness* 0 - 2 max.5 mm
Specific Surface Area (Blaine) 3500 - 4000 - cm2/g
Bulk Density 940 - 1000 - g/l
2 Days Strength 24,0 - 32,0 min.20,0 MPa
28 Days Strength 55,0 - 65,0 min.52,5 MPa

Chemical Properties

Nuh Çimento San. A.Ş. Standard Unit
SO3* 2,20 - 2,80 max.3,00 %
S2-* 0 max.0,20 %
MgO* 1,20 - 1,80 max.3,00 %
Al2O3* 4,50 - 5,10 max.8,00 %
Loss on Ignition 1,90 - 2,80 max.5,00 %
Insoluble Residue 0,10 - 1,00 max.5,00 %
Cl- <0,05 max.0,10 %
Alkali equivalent Na2O + 0.658 K2O 0,40 - 0,80 - %
Free Lime 0,80 - 1,50 - %
C3A* 5,00 - 8,00 max.10,00 %
[C3A + 0.27 C3S]* 19,0 - 22,5 max.23,5 %

(1) Cement: It is manufactured to be resistant to sea water according to French standard NF P 15-317. That’s why the “*” sign features; NF P 15-317.

* Can be available with Low Hexavalent Chromium content (below 2 ppm) and Low Alkali Equivalent content (below 0,60 %).

It can be put on the market as bulk, in 1,5 ton big bags, in sling bags and also in 25 and 50 kg bags.

PACKAGING

Our product has EC certificate given by the Council for Quality and Environment (CQE) and has the right to use CE mark.

QUALITY CONTROL

Abdulhamit AKÇAY, Sales Director ( Export ), Internal Telephone 2075

FOR INFORMATION

It is updated on 28/02/2020.

UPDATE

The product specifications described above are intended solely for the purpose of informing customers and our company does not assume any responsibility.

CEM I 42,5 R - SR5

PRODUCTS

EN 197-1:2011

STANDARD

28/02/2020

UPDATE

CEM I 42,5 5R-SR5 is the product which is obtained by griding clinker, w hich is acquired by mixing raw materials like limes tone, marl, clay, iron ore, pyrite ash, bauxite etc. at appropriate rates, grinding and boiling them, with an amount of reamer (generally gypsum) and mixing it with water and which gains resistance by freezing up in a certain time.

It may be generally used in areas where normal portland cements are used and it is also suitable for use in areas exposed to sulphated water like like dam constructions, tunnels, port constructions, irrigation channels, construction chemicals as the amount of C3A is below 5%.

Physical Properties

Nuh Çimento San. A.Ş. Standard Unit
Initial Setting Time 130 - 180 min.60 minute
Final Setting Time 170 - 240 - minute
Specific Gravity 3,19 - 3,23 - g/cm3
Soundness 0 - 2 max.10 mm
Specific Surface Area (Blaine) 3500 - 3800 - cm2/g
Bulk Density 960 - 1020 - g/l
2 Days Strength 25,0 - 35,0 min.20 MPa
28 Days Strength 54,0 - 60,0 42,5-62,5 MPa

Chemical Properties

Nuh Çimento San. A.Ş. Standard Unit
SO3 2,40 - 3,00 max.4,00 %
MgO 1,20 - 1,80 - %
Loss on Ignition 1,20 - 2,10 max.5,00 %
Insoluble Residue 0,20 - 0,80 max.5,00 %
Cl- <0,05 max.0,10 %
Alkali equivalent Na2O + 0.658 K2O 0,40 - 0,70 - %
Free Lime 1,00 - 1,50 - %
C3A 2,50 - 4,80 max.5,00 %
(2xC3A) + C4AF 19,0 - 23,0 max.25 %
C3S 50,0 - 58,0 - %

* Can be available with Low Hexavalent Chromium content (below 2 ppm) and Low Alkali Equivalent content (below 0,60 %).

It can be put on the market as bulk, in 1,5 ton big bags, in sling bags and also in 25 and 50 kg bags.

PACKAGING

Our product has EC certificate given by the Council for Quality and Environment (CQE) and has the right to use CE mark.

QUALITY CONTROL

Abdulhamit AKÇAY, Sales Director ( Export ), Internal Telephone 2075

FOR INFORMATION

It is updated on 28/02/2020.

UPDATE

The product specifications described above are intended solely for the purpose of informing customers and our company does not assume any responsibility.

CEM II/A-S 42,5 R

PRODUCTS

EN 197-1:2011

STANDARD

28/02/2020

UPDATE

It is obtained by grinding a certain amount of portland cement clinker with mineral additives (slag) at proportions (maximum 20%) defined in respective standards with rea mer (gypsum) and gains resistance by freezing a while after it is mixed with water.

It is generally used in all practices where portland cement is used. Its hydration heat is lower than portland cement. It is suitable for use in concrete works in aggressive environments containing ions like sulphide and/or chloride.

Physical Properties

Nuh Çimento San. A.Ş. Standard Unit
Initial Setting Time 100-150 min.60 minute
Final Setting Time 150-200 - minute
Soundness 0 - 2 max.10 mm
Specific Surface Area (Blaine) 4000- 4500 - cm2/g
Bulk Density 900-1000 - g/l
2 Days Strength 27,0 - 34,0 min.20,0 MPa
28 Days Strength 55,0 - 61,0 42,5-62,5 MPa

Chemical Properties

Nuh Çimento San. A.Ş. Standard Unit
SO3 2,30 - 2,90 max.4,00 %
Cl- <0,05 max.0,10 %

* Can be available with Low Hexavalent Chromium content (below 2 ppm) and Low Alkali Equivalent content (below 0,60 %).

It can be put on the market as bulk, in 1,5 ton big bags, in sling bags and also in 25 and 50 kg bags.

PACKAGING

Our product has EC certificate given by the Council for Quality and Environment (CQE) and has the right to use CE mark.

QUALITY CONTROL

Abdulhamit AKÇAY, Sales Director ( Export ), Internal Telephone 2075

FOR INFORMATION

It is updated on 28/02/2020.

UPDATE

The product specifications described above are intended solely for the purpose of informing customers and our company does not assume any responsibility.

CEM II/B-S 42,5 R

PRODUCTS

EN 197-1:2011

STANDARD

28/02/2020

UPDATE

The cement is produced by grinding a mixture of additives (slag) prescribed by standards (min. % 21, max. % 35) with portland cement clinker by addition of a certain amount of retarder (generally gypsum) and sets and gains strength after a certain time being mixed with water.

Generally the product can be used in all places where portland cement is applicable. Hydration heat is relatively lower than that of portland cement. It can deliver best results especially in concrete works performed in aggresive areas where the content of sulphate and/or chloride is higher.

Physical Properties

Nuh Çimento San. A.Ş. Standard Unit
Initial Setting Time 120-160 min.60 minute
Final Setting Time 180-240 - minute
Soundness 0 - 2 max.10 mm
Specific Surface Area (Blaine) 4400 - 4900 - cm2/g
Bulk Density 940 - 980 - g/l
2 Days Strength 25,0 - 30,0 min.20,0 MPa
28 Days Strength 54,0 - 59,0 42,5-62,5 MPa

Chemical Properties

Nuh Çimento San. A.Ş. Standard Unit
SO3 2,40 - 2,80 max.4,00 %
Cl- <0,05 max.0,10 %

* Can be available with Low Hexavalent Chromium content (below 2 ppm) and Low Alkali Equivalent content (below 0,60 %).

It can be put on the market as bulk, in 1,5 ton big bags, in sling bags and also in 25 and 50 kg bags.

PACKAGING

Our product has EC certificate given by the Council for Quality and Environment (CQE) and has the right to use CE mark.

QUALITY CONTROL

Abdulhamit AKÇAY, Sales Director ( Export ), Internal Telephone 2075

FOR INFORMATION

It is updated on 28/02/2020.

UPDATE

The product specifications described above are intended solely for the purpose of informing customers and our company does not assume any responsibility.

CEM II/C-M (P-LL) 32,5 R

PRODUCTS

TS EN 197-5:2021

STANDARD

September 2021

UPDATE

The product contains 50-64% clinker, 18-30% natural pozzolana, 6-20% limestone, 0-5% minor additional components. It is a type of blended cement obtained by grinding portland cement clinker with mineral additive and gypsum as a retarder.

The product delivers the strength values respectively in late periods compared to CEM I and CEM II types. Water/cement ratio is respectively higher. It is much more resistant to alkali and aggretage reactions. It is best for repairing works, foundation filling and used in stucco and building chemicals manufacturing.

Physical Properties

Nuh Çimento San. A.Ş. Standard Unit
Initial Setting Time 150 - 200 min.75 minute
Final Setting Time 200 - 300 minute
Soundness 0 - 2 max.10 mm
Specific Surface Area (Blaine) 5000 - 5500 - cm2/g
Bulk Density 800 - 900 - g/l
7 Days Strength 18,0 - 22,0 min.16,0 MPa
28 Days Strength 34,0 - 42,0 32,5 - 52,5 MPa

Chemical Properties

Nuh Çimento San. A.Ş. Standard Unit
SO3 2,30 - 2,80 max.4,0 %
Cl- <0,05 max.0,10 %

* Can be available with Low Hexavalent Chromium content (below 2 ppm).

It can be put on the market as bulk, in 1,5 ton big bags, in sling bags and also in 25 and 50 kg bags.

PACKAGING

Our product is certified by CPC according to TS EN 197-5:2021 and has the right to use the G mark.

QUALITY CONTROL

Abdulhamit AKÇAY, Sales Director ( Export ), Internal Telephone 2075

FOR INFORMATION

UPDATE

The product specifications described above are intended solely for the purpose of informing customers and our company does not assume any responsibility.

OWC

PRODUCTS

API Spec 10A& Q1

STANDARD

28/02/2020

UPDATE

Type G cement is the product obtained by grinding portland cement clinker with one or more types of calcium sufates with portland cement clinker. No additives can be used during production of Type G oil well cement except clinker and calcium sulfate This type of cement is aimed to be used as oil well cement basically.

Type G Oil Well Cement has high sulfate-resistant (HSR) and moderate sulfate-resistant (MSR) grades. In Nuh Cement only HSR grade is produced.

Physical Properties

Nuh Çimento San. A.Ş. Standard Unit
Compressive strength after 8 hours curing at 38 oC at atmospheric pressure 3,0-5,0 min.2,1 MPa
Compressive strength after 8 hours curing at 60 oC at atmospheric pressure 12,0-15,0 min.10,3 MPa
Free fluid content 4,5-5,5 max.5,9 %
Maximum consistency (15 min. to 30 min.) 17-22 max.30 Bc
Thickening time (100 Bc) 95-115 90 - 120 minute

Chemical Properties

Nuh Çimento San. A.Ş. Standard Unit
SO3 2,10-2,50 max.3,00 %
MgO 1,20-1,60 max.6,00 %
Loss on Ignition 1,00-1,50 max.3,00 %
Insoluble Residue 0,20-0,60 max.0,75 %
Tricalcium silicate (C3S) 55,0-60,0 48,0 - 65,0 %
Tricalcium aluminate (C3A) 1,50-2,50 max.3,00 %
Tetracalcium aluminoferrite (C4AF) + 2 x [Tricalcium aluminate (C3A)] 18-22 max.24 %
Alkali Equivalent Na2O + 0.658 K2O 0,45-0,55 max.0,75 %

* Can be available with Low Hexavalent Chromium content (below 2 ppm).

It is put on the market as bulk and in 1,5 ton big bags.

PACKAGING

Our product has Certificate of Authority to Use The Official API Monogram given by American Petroleum Institute and has the right to use API Monogram mark.

QUALITY CONTROL

Abdulhamit AKÇAY, Sales Director ( Export ), Internal Telephone 2075

FOR INFORMATION

It is updated on 28/02/2020.

UPDATE

The product specifications described above are intended solely for the purpose of informing customers and our company does not assume any responsibility.

GROUND GRANULATED BLAST FURNACE SLAG

PRODUCTS

TS EN 15167-1:2006

STANDARD

28/02/2020

UPDATE

The glassy material which is obtained by rapid cooling of the molten slag in the appropriate composition obtained when melting and refining in an iron ore furnace, containing glass slag at least 2/3 of the mass and exhibiting hydraulic properties when properly activated.

Ground granulated blast furnace slag; Fine dust obtained by grinding grain blast furnace slag.

Ground Granulated Blast Furnace Slag

Nuh Çimento San. A.Ş. Standard Unit
MgO 6,00-8,00 max.18,00 %
S-2 0,00-0,02 max.2,00 %
SO3 0,80-1,80 max.2,50 %
Loss on Ignition 0,10-1,00 max.3,00 %
Cl- 0,0050-0,0100 max.0,10 %
Moisture 0,10-0,60 max.1,00 %
Specific Surface Area (Blaine) 4000-5000 min.2750 cm2/g

Reference Cement Properties

Nuh Çimento San. A.Ş. Standard Unit
Specific Surface Area (Blaine) 3700-4100 min.3000 cm2/g
C3A 6,00-8,00 6,00 - 12,00 %
Alkali equivalent Na2O + 0.658 K2O 0,55-1,00 0,50 - 1,20 %

50 % Reference Cement, 50 % Ground Granulated Blast Furnace Slag By Mass

Nuh Çimento San. A.Ş. Standard Unit
7 Days Activity Index 46-52 min.45 %
28 Days Activity Index 71-75 min.70 %

It is put on the market as bulk and in 1.5 ton big bags.

PACKAGING

Our product has Certificate of Constancy of Performance given by CPC and has the right to use CE mark.

QUALITY CONTROL

Abdulhamit AKÇAY, Sales Director ( Export ), Internal Telephone 2075

FOR INFORMATION

It is updated on 28/02/2020.

UPDATE

The product specifications described above are intended solely for the purpose of informing customers and our company does not assume any responsibility.

Early History and Development of Portland Cement


Since the first constitution of civilizations, a material has been sought to bind the stones in solid form. The Assyrians and the Babylonians used clay for this purpose, and in Egyptians, they developed lime and gypsum mortar as binding material in the construction of structures such as Pyramids. The Greeks further developed the binding materials, and eventually the Romans introduced the cement producing structures that provided continuous strength. Most of the building foundations in the Roman forum were built in mortar form at a depth of 3.5 meters in some places. The great Roman baths, Colosseum and Basilica of Constantine, built around BC.27, are examples of early Roman architecture using cement mortar.